Bambu Lab PA6-CF Filament (non-AMS Compatible)
Bambu Lab PA6-CF is a carbon fiber-reinforced PA6 (Nylon 6) filament.
The carbon fiber reinforcement provides significantly high rigidity and strength properties in dry environments and offers exceptional heat resistance and impact strength. Similar to other Bambu CF filaments, these outstanding mechanical properties make it an ideal choice for printing fixtures, brackets, automotive and mechanical components, and various structural and engineering parts used in dry environments.
Outstanding Strength and Rigidity
As a new member of Bambu high-performance filaments, PA6-CF boasts excellent stiffness and strength properties in dry environments, perfect for printing load-bearing structural components.
Normal PA-CF | PA6-CF | Improvement % | |
Strength (Bending Strength - XY, dry state) | 128 MPa | 151 MPa | 18% |
Stiffness (Bending Modulus - XY, dry state) | 4420 MPa | 5460 MPa | 24% |
Shock and Vibration Resistance
Bambu Lab PA6-CF provides excellent impact resistance and ensures effective vibration resistance for your prints. It is commonly used for printing models that need to withstand shocks, collisions, and vibrations.
* PA6-CF prints become tougher if stored in a humid environment for more than 1 day.
Exceptional Heat Resistance
Filament | PLA Basic | PETG Basic | ABS | ASA | PC | PA6-CF | PAHT-CF | PET-CF |
Heat Deflection Temperature / ℃ (0.45 MPa) | 57 ℃ | 69 ℃ | 87 ℃ | 100 ℃ | 117 ℃ | 186 ℃ | 194 ℃ | 205 ℃ |
Parameter Comparison
Normal PA6-CF | PA6-CF | PAHT-CF | |
Composition | Nylon 6, Carbon Fiber | Nylon 6, Carbon Fiber | PA12 and other long-chain PA, Carbon Fiber |
AMS Compatibility | NO | NO | YES |
Dry Out Before Use | Required | Required | Required |
Printing Speed | < 100 mm/s | < 100 mm/s | < 100 mm/s |
Printer Type | Enclosure | Enclosure | Enclosure |
Toughness (Impact Strength - XY, dry state) | 35.7 kJ/m² | 40.3 kJ/m² | 57.5 kJ/m² |
Toughness (Impact Strength - XY, wet state) | 65.4 kJ/m² | 57.2 kJ/m² | 62.3 kJ/m² |
Strength (Bending Strength - XY, dry state) | 141 MPa | 151 MPa | 125 MPa |
Strength (Bending Strength - XY, wet state) | 67 MPa | 95 MPa | 115 MPa |
Layer Strength (Bending Strength - Z, dry state) | 72 MPa | 80 MPa | 61 MPa |
Layer Strength (Bending Strength - Z, wet state) | 31 MPa | 45 MPa | 49 MPa |
Stiffness (Bending Modulus - XY, dry state) | 4870 MPa | 5460 MPa | 4230 MPa |
Stiffness (Bending Modulus - XY, wet state) | 1890 MPa | 3560 MPa | 3640 MPa |
Layer Adhesion (Impact Strength - Z, dry state) | 11.6 kJ/m² | 15.5 kJ/m² | 13.3 kJ/m² |
Heat Resistant (HDT, 0.45 MPa) | 177 ℃ | 186 ℃ | 194 ℃ |
Saturation Water Absorption Rate / % (25 °C, 55% RH) | 3.80 | 2.35 | 0.88 |
Recommended Printing Settings | |
Dry Settings before Printing | 80 °C, 8 - 12 hours |
Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
Nozzle Temperature | 260 - 290 °C |
Bed Temperature (with Glue) | 80 - 100 °C |
Printing Speed | < 100 mm/s |
Physical Properties | |
Density | 1.09 g/cm³ |
Vicat Softening Temperature | 212 °C |
Heat Deflection Temperature | 186 °C |
Melting Temperature | 223 °C |
Melt Index | 6.8 ± 0.6 g/10 min |
Mechanical Properties | |
Tensile Strength | 102 ± 7 MPa |
Breaking Elongation Rate | 5.8 ± 1.6 % |
Bending Modulus | 5460 ± 280 MPa |
Bending Strength | 151 ± 8 MPa |
Impact Strength | 40.3 ± 2.5 kJ/m² |
Art: | Filament |
Property: | Faserverstärkt |
Material: | PA CF |
Color: | black |
Radius: | 1,75 mm |
Weight: | 500 g, 1000 g |